I would probably agree that it is casing marks. If you want to be absolutely sure then you can use a penetrating dye (like iodine) and see if it bleeds through the casing. Similar to a magna flux to test welds, but much cheaper. You can use most any small molecular liquid (like white gas with a colour added), these have a tendency to bleed through a crack in metal.